© 2020 Elsevier Ltd A laser technology has been developed for fabricating structures from composite layers based on biopolymers: albumin, collagen, and chitosan with single-walled carbon nanotubes (SWCNT). The structures are intended for cardiovascular devices and tissue-engineered implants. This is evidenced by the results of studies. The composite layers were fabricated due to the phase transition of biopolymers and SWCNT aqueous dispersion under the influence of laser pulses. At the same time branched 3D networks of SWCNT were formed in the biopolymer matrix. The threshold energy fluence of laser pulses was determined (0.032–0.083 J/cm2) at which a bimodal distribution of pores was observed. The calculation of contact resistances between nanotubes at percolation units of 3D networks (20–100 kOhm) was carried out. Composite layers fabricated by laser demonstrated conductivity values that were higher (12.4 S/m) than those for layers by thermostat (4.7 S/m). The maximum hardness of the composite layers with SWCNT (0.01 wt%) by laser was 482 ± 10, 425 ± 10, and 407 ± 15 MPa for albumin, collagen and chitosan, respectively. The hardness of the thermostat layers was less than 100 MPa. The viability of endothelial cells in composite layers was improved. The composite layers ensured a normal level of hemolysis during interaction with erythrocytes.

© 2019 Elsevier B.V. The results of the study of composites based on bovine serum albumin (BSA) and single-walled carbon nanotubes (SWCNT) are presented. Nanocomposites were created by evaporation of the water-albumin dispersion with nanotubes using diode laser with temperature control. Two types of nanotubes were used. SWCNT I were synthesized using the electric arc method, SWCNT II were synthesized using the gas phase method. SWCNT I had a diameter and length less than SWCNT II. The mechanism of interaction between BSA and SWCNT in solid nanocomposites is considered. An experimental and theoretical studies of the interaction between aspartic (Asp) and glutamic (Glu) amino acids located on the outer surface of BSA and nanotubes using of vibrational spectroscopy (Fourier-transform infrared (FTIR) and Raman spectroscopy) was carried out. The possibility of nanotubes functionalization by oxygen atoms of negative amino acid residues Asp and Glu, which are on the outer surface of BSA, is shown by molecular modeling. The formation of covalent bonds between BSA and SWCNT in nanocomposites with different concentrations of nanotubes (0.01, 0.1 and 1 g/l) was confirmed by vibrational spectra. The covalent interaction between BSA with SWCNT under the laser irradiation leads to the conformational changes in the secondary and tertiary structures of albumin. This is confirmed by a significant decrease in the intensity of the absorption bands in the high-frequency region. The calculation of the vibrational spectra of the three Glycine:Glycine, Glutamic acid:Threonine and Aspartic acid:Lysine complexes, which take into account hydrogen, ion-dipole and ion-ion bonds, showed that a disturbance in the intermolecular interaction between amino acid residues led to significant decrease in the intensity of absorption bands in the region of stretching vibrations bonds OH and NH. From the Raman spectra, it was found that a significant number of defects in SWCNT is caused by the covalent attachment of oxygen atoms to the graphene surface of nanotubes. An increase in the diameter of nanotubes (4 nm) has practically no effect on the absorption spectrum of nanocomposite, while measuring the concentration of SWCNT affects the FTIR spectra. This confirmed the hydrophobic interaction between BSA and SWCNT. Thus, it was shown that BSA solid nanocomposites with CNTs can interact either with the help of hydrophobic forces or with the formation of covalent bonds, which depends on the diameter of the used nanotubes. The viability of connective fibroblast tissue cells on nanocomposites with both types of SWCNT was demonstrated. It was found that nanocomposites based on SWCNT I provide slightly better compatibility of their structure with fibroblasts. It allows to achieve better cell adhesion to the nanocomposite surface. These criteria make extensive use of scaffold nanocomposites in biomedicine, depending on the requirements for their quality and application.

© 2019 Elsevier B.V. The results of the study of composites based on bovine serum albumin (BSA) and single-walled carbon nanotubes (SWCNT) are presented. Nanocomposites were created by evaporation of the water-albumin dispersion with nanotubes using diode laser with temperature control. Two types of nanotubes were used. SWCNT I were synthesized using the electric arc method, SWCNT II were synthesized using the gas phase method. SWCNT I had a diameter and length less than SWCNT II. The mechanism of interaction between BSA and SWCNT in solid nanocomposites is considered. An experimental and theoretical studies of the interaction between aspartic (Asp) and glutamic (Glu) amino acids located on the outer surface of BSA and nanotubes using of vibrational spectroscopy (Fourier-transform infrared (FTIR) and Raman spectroscopy) was carried out. The possibility of nanotubes functionalization by oxygen atoms of negative amino acid residues Asp and Glu, which are on the outer surface of BSA, is shown by molecular modeling. The formation of covalent bonds between BSA and SWCNT in nanocomposites with different concentrations of nanotubes (0.01, 0.1 and 1 g/l) was confirmed by vibrational spectra. The covalent interaction between BSA with SWCNT under the laser irradiation leads to the conformational changes in the secondary and tertiary structures of albumin. This is confirmed by a significant decrease in the intensity of the absorption bands in the high-frequency region. The calculation of the vibrational spectra of the three Glycine:Glycine, Glutamic acid:Threonine and Aspartic acid:Lysine complexes, which take into account hydrogen, ion-dipole and ion-ion bonds, showed that a disturbance in the intermolecular interaction between amino acid residues led to significant decrease in the intensity of absorption bands in the region of stretching vibrations bonds OH and NH. From the Raman spectra, it was found that a significant number of defects in SWCNT is caused by the covalent attachment of oxygen atoms to the graphene surface of nanotubes. An increase in the diameter of nanotubes (4 nm) has practically no effect on the absorption spectrum of nanocomposite, while measuring the concentration of SWCNT affects the FTIR spectra. This confirmed the hydrophobic interaction between BSA and SWCNT. Thus, it was shown that BSA solid nanocomposites with CNTs can interact either with the help of hydrophobic forces or with the formation of covalent bonds, which depends on the diameter of the used nanotubes. The viability of connective fibroblast tissue cells on nanocomposites with both types of SWCNT was demonstrated. It was found that nanocomposites based on SWCNT I provide slightly better compatibility of their structure with fibroblasts. It allows to achieve better cell adhesion to the nanocomposite surface. These criteria make extensive use of scaffold nanocomposites in biomedicine, depending on the requirements for their quality and application.

© 2019 Elsevier B.V. The results of the study of composites based on bovine serum albumin (BSA) and single-walled carbon nanotubes (SWCNT) are presented. Nanocomposites were created by evaporation of the water-albumin dispersion with nanotubes using diode laser with temperature control. Two types of nanotubes were used. SWCNT I were synthesized using the electric arc method, SWCNT II were synthesized using the gas phase method. SWCNT I had a diameter and length less than SWCNT II. The mechanism of interaction between BSA and SWCNT in solid nanocomposites is considered. An experimental and theoretical studies of the interaction between aspartic (Asp) and glutamic (Glu) amino acids located on the outer surface of BSA and nanotubes using of vibrational spectroscopy (Fourier-transform infrared (FTIR) and Raman spectroscopy) was carried out. The possibility of nanotubes functionalization by oxygen atoms of negative amino acid residues Asp and Glu, which are on the outer surface of BSA, is shown by molecular modeling. The formation of covalent bonds between BSA and SWCNT in nanocomposites with different concentrations of nanotubes (0.01, 0.1 and 1 g/l) was confirmed by vibrational spectra. The covalent interaction between BSA with SWCNT under the laser irradiation leads to the conformational changes in the secondary and tertiary structures of albumin. This is confirmed by a significant decrease in the intensity of the absorption bands in the high-frequency region. The calculation of the vibrational spectra of the three Glycine:Glycine, Glutamic acid:Threonine and Aspartic acid:Lysine complexes, which take into account hydrogen, ion-dipole and ion-ion bonds, showed that a disturbance in the intermolecular interaction between amino acid residues led to significant decrease in the intensity of absorption bands in the region of stretching vibrations bonds OH and NH. From the Raman spectra, it was found that a significant number of defects in SWCNT is caused by the covalent attachment of oxygen atoms to the graphene surface of nanotubes. An increase in the diameter of nanotubes (4 nm) has practically no effect on the absorption spectrum of nanocomposite, while measuring the concentration of SWCNT affects the FTIR spectra. This confirmed the hydrophobic interaction between BSA and SWCNT. Thus, it was shown that BSA solid nanocomposites with CNTs can interact either with the help of hydrophobic forces or with the formation of covalent bonds, which depends on the diameter of the used nanotubes. The viability of connective fibroblast tissue cells on nanocomposites with both types of SWCNT was demonstrated. It was found that nanocomposites based on SWCNT I provide slightly better compatibility of their structure with fibroblasts. It allows to achieve better cell adhesion to the nanocomposite surface. These criteria make extensive use of scaffold nanocomposites in biomedicine, depending on the requirements for their quality and application.

© 2019 Elsevier B.V. The results of the study of composites based on bovine serum albumin (BSA) and single-walled carbon nanotubes (SWCNT) are presented. Nanocomposites were created by evaporation of the water-albumin dispersion with nanotubes using diode laser with temperature control. Two types of nanotubes were used. SWCNT I were synthesized using the electric arc method, SWCNT II were synthesized using the gas phase method. SWCNT I had a diameter and length less than SWCNT II. The mechanism of interaction between BSA and SWCNT in solid nanocomposites is considered. An experimental and theoretical studies of the interaction between aspartic (Asp) and glutamic (Glu) amino acids located on the outer surface of BSA and nanotubes using of vibrational spectroscopy (Fourier-transform infrared (FTIR) and Raman spectroscopy) was carried out. The possibility of nanotubes functionalization by oxygen atoms of negative amino acid residues Asp and Glu, which are on the outer surface of BSA, is shown by molecular modeling. The formation of covalent bonds between BSA and SWCNT in nanocomposites with different concentrations of nanotubes (0.01, 0.1 and 1 g/l) was confirmed by vibrational spectra. The covalent interaction between BSA with SWCNT under the laser irradiation leads to the conformational changes in the secondary and tertiary structures of albumin. This is confirmed by a significant decrease in the intensity of the absorption bands in the high-frequency region. The calculation of the vibrational spectra of the three Glycine:Glycine, Glutamic acid:Threonine and Aspartic acid:Lysine complexes, which take into account hydrogen, ion-dipole and ion-ion bonds, showed that a disturbance in the intermolecular interaction between amino acid residues led to significant decrease in the intensity of absorption bands in the region of stretching vibrations bonds OH and NH. From the Raman spectra, it was found that a significant number of defects in SWCNT is caused by the covalent attachment of oxygen atoms to the graphene surface of nanotubes. An increase in the diameter of nanotubes (4 nm) has practically no effect on the absorption spectrum of nanocomposite, while measuring the concentration of SWCNT affects the FTIR spectra. This confirmed the hydrophobic interaction between BSA and SWCNT. Thus, it was shown that BSA solid nanocomposites with CNTs can interact either with the help of hydrophobic forces or with the formation of covalent bonds, which depends on the diameter of the used nanotubes. The viability of connective fibroblast tissue cells on nanocomposites with both types of SWCNT was demonstrated. It was found that nanocomposites based on SWCNT I provide slightly better compatibility of their structure with fibroblasts. It allows to achieve better cell adhesion to the nanocomposite surface. These criteria make extensive use of scaffold nanocomposites in biomedicine, depending on the requirements for their quality and application.

© 2019 Elsevier B.V. The results of the study of composites based on bovine serum albumin (BSA) and single-walled carbon nanotubes (SWCNT) are presented. Nanocomposites were created by evaporation of the water-albumin dispersion with nanotubes using diode laser with temperature control. Two types of nanotubes were used. SWCNT I were synthesized using the electric arc method, SWCNT II were synthesized using the gas phase method. SWCNT I had a diameter and length less than SWCNT II. The mechanism of interaction between BSA and SWCNT in solid nanocomposites is considered. An experimental and theoretical studies of the interaction between aspartic (Asp) and glutamic (Glu) amino acids located on the outer surface of BSA and nanotubes using of vibrational spectroscopy (Fourier-transform infrared (FTIR) and Raman spectroscopy) was carried out. The possibility of nanotubes functionalization by oxygen atoms of negative amino acid residues Asp and Glu, which are on the outer surface of BSA, is shown by molecular modeling. The formation of covalent bonds between BSA and SWCNT in nanocomposites with different concentrations of nanotubes (0.01, 0.1 and 1 g/l) was confirmed by vibrational spectra. The covalent interaction between BSA with SWCNT under the laser irradiation leads to the conformational changes in the secondary and tertiary structures of albumin. This is confirmed by a significant decrease in the intensity of the absorption bands in the high-frequency region. The calculation of the vibrational spectra of the three Glycine:Glycine, Glutamic acid:Threonine and Aspartic acid:Lysine complexes, which take into account hydrogen, ion-dipole and ion-ion bonds, showed that a disturbance in the intermolecular interaction between amino acid residues led to significant decrease in the intensity of absorption bands in the region of stretching vibrations bonds OH and NH. From the Raman spectra, it was found that a significant number of defects in SWCNT is caused by the covalent attachment of oxygen atoms to the graphene surface of nanotubes. An increase in the diameter of nanotubes (4 nm) has practically no effect on the absorption spectrum of nanocomposite, while measuring the concentration of SWCNT affects the FTIR spectra. This confirmed the hydrophobic interaction between BSA and SWCNT. Thus, it was shown that BSA solid nanocomposites with CNTs can interact either with the help of hydrophobic forces or with the formation of covalent bonds, which depends on the diameter of the used nanotubes. The viability of connective fibroblast tissue cells on nanocomposites with both types of SWCNT was demonstrated. It was found that nanocomposites based on SWCNT I provide slightly better compatibility of their structure with fibroblasts. It allows to achieve better cell adhesion to the nanocomposite surface. These criteria make extensive use of scaffold nanocomposites in biomedicine, depending on the requirements for their quality and application.

© 2019 Elsevier B.V. The results of the study of composites based on bovine serum albumin (BSA) and single-walled carbon nanotubes (SWCNT) are presented. Nanocomposites were created by evaporation of the water-albumin dispersion with nanotubes using diode laser with temperature control. Two types of nanotubes were used. SWCNT I were synthesized using the electric arc method, SWCNT II were synthesized using the gas phase method. SWCNT I had a diameter and length less than SWCNT II. The mechanism of interaction between BSA and SWCNT in solid nanocomposites is considered. An experimental and theoretical studies of the interaction between aspartic (Asp) and glutamic (Glu) amino acids located on the outer surface of BSA and nanotubes using of vibrational spectroscopy (Fourier-transform infrared (FTIR) and Raman spectroscopy) was carried out. The possibility of nanotubes functionalization by oxygen atoms of negative amino acid residues Asp and Glu, which are on the outer surface of BSA, is shown by molecular modeling. The formation of covalent bonds between BSA and SWCNT in nanocomposites with different concentrations of nanotubes (0.01, 0.1 and 1 g/l) was confirmed by vibrational spectra. The covalent interaction between BSA with SWCNT under the laser irradiation leads to the conformational changes in the secondary and tertiary structures of albumin. This is confirmed by a significant decrease in the intensity of the absorption bands in the high-frequency region. The calculation of the vibrational spectra of the three Glycine:Glycine, Glutamic acid:Threonine and Aspartic acid:Lysine complexes, which take into account hydrogen, ion-dipole and ion-ion bonds, showed that a disturbance in the intermolecular interaction between amino acid residues led to significant decrease in the intensity of absorption bands in the region of stretching vibrations bonds OH and NH. From the Raman spectra, it was found that a significant number of defects in SWCNT is caused by the covalent attachment of oxygen atoms to the graphene surface of nanotubes. An increase in the diameter of nanotubes (4 nm) has practically no effect on the absorption spectrum of nanocomposite, while measuring the concentration of SWCNT affects the FTIR spectra. This confirmed the hydrophobic interaction between BSA and SWCNT. Thus, it was shown that BSA solid nanocomposites with CNTs can interact either with the help of hydrophobic forces or with the formation of covalent bonds, which depends on the diameter of the used nanotubes. The viability of connective fibroblast tissue cells on nanocomposites with both types of SWCNT was demonstrated. It was found that nanocomposites based on SWCNT I provide slightly better compatibility of their structure with fibroblasts. It allows to achieve better cell adhesion to the nanocomposite surface. These criteria make extensive use of scaffold nanocomposites in biomedicine, depending on the requirements for their quality and application.

© 2019 Elsevier B.V. The results of the study of composites based on bovine serum albumin (BSA) and single-walled carbon nanotubes (SWCNT) are presented. Nanocomposites were created by evaporation of the water-albumin dispersion with nanotubes using diode laser with temperature control. Two types of nanotubes were used. SWCNT I were synthesized using the electric arc method, SWCNT II were synthesized using the gas phase method. SWCNT I had a diameter and length less than SWCNT II. The mechanism of interaction between BSA and SWCNT in solid nanocomposites is considered. An experimental and theoretical studies of the interaction between aspartic (Asp) and glutamic (Glu) amino acids located on the outer surface of BSA and nanotubes using of vibrational spectroscopy (Fourier-transform infrared (FTIR) and Raman spectroscopy) was carried out. The possibility of nanotubes functionalization by oxygen atoms of negative amino acid residues Asp and Glu, which are on the outer surface of BSA, is shown by molecular modeling. The formation of covalent bonds between BSA and SWCNT in nanocomposites with different concentrations of nanotubes (0.01, 0.1 and 1 g/l) was confirmed by vibrational spectra. The covalent interaction between BSA with SWCNT under the laser irradiation leads to the conformational changes in the secondary and tertiary structures of albumin. This is confirmed by a significant decrease in the intensity of the absorption bands in the high-frequency region. The calculation of the vibrational spectra of the three Glycine:Glycine, Glutamic acid:Threonine and Aspartic acid:Lysine complexes, which take into account hydrogen, ion-dipole and ion-ion bonds, showed that a disturbance in the intermolecular interaction between amino acid residues led to significant decrease in the intensity of absorption bands in the region of stretching vibrations bonds OH and NH. From the Raman spectra, it was found that a significant number of defects in SWCNT is caused by the covalent attachment of oxygen atoms to the graphene surface of nanotubes. An increase in the diameter of nanotubes (4 nm) has practically no effect on the absorption spectrum of nanocomposite, while measuring the concentration of SWCNT affects the FTIR spectra. This confirmed the hydrophobic interaction between BSA and SWCNT. Thus, it was shown that BSA solid nanocomposites with CNTs can interact either with the help of hydrophobic forces or with the formation of covalent bonds, which depends on the diameter of the used nanotubes. The viability of connective fibroblast tissue cells on nanocomposites with both types of SWCNT was demonstrated. It was found that nanocomposites based on SWCNT I provide slightly better compatibility of their structure with fibroblasts. It allows to achieve better cell adhesion to the nanocomposite surface. These criteria make extensive use of scaffold nanocomposites in biomedicine, depending on the requirements for their quality and application.

© 2019 by the authors. This paper reveals the mechanism of nanowelding a branched network of single-walled carbon nanotubes (SWCNTs) used as a framework for the formation of protein-polymer matrices with albumin, collagen, and chitosan. It is shown that the introduction of certain point defects into the structure of SWCNTs (single vacancy, double vacancy, Stone-Wales defect, and a mixed defect) allows us to obtain strong heating in defective regions as compared to ideal SWCNTs. The wavelengths at which absorption reaches 50% are determined. Non-uniform absorption of laser radiation along with inefficient heat removal in defective regions determines the formation of hot spots, in which nanowelding of SWCNTs is observed even at 0.36 nm between contacting surfaces. The regularities of formation of layered protein-polymer matrices and the features of their interaction with cell membrane are revealed. All studies are carried out in silico using high-precision quantum approaches.

© 2018 IOP Publishing Ltd. The integration of energy harvesting and energy storage in a single device both enables the conversion of ambient energy into electricity and provides a sustainable power source for various electronic devices and systems. On the other hand, mechanical flexibility, coupled with optical transparency of the energy storage devices, is required for many applications, ranging from self-powered rolled-up displays to wearable optoelectronic devices. We integrate a piezoelectric poly(vinylidene-trifluoroethylene) (P(VDF-TrFE)) film into a flexible supercapacitor system to harvest and store the energy. The asymmetric output characteristics of the piezoelectric P(VDF-TrFE) film under mechanical impacts results in effective charging of the supercapacitors. The integrated piezo-supercapacitor exhibits a specific capacitance of 50 F g-1. The open-circuit voltage of the flexible and transparent supercapacitor reached 500 mV within 20 s during the mechanical action. Our hybridized energy harvesting and storage device can be further extended to provide a sustainable power source for various types of sensors integrated into wearable units.

© 2018 SPIE. The conductivity of layers (thickness ∼ 0.5-20 μm) of composite nanomaterials consisting of bovine serum albumin (BSA) with single-walled carbon nanotubes (SWCNTs) has been studied. The BSA/SWCNT composite nanomaterial was prepared according to a route map, some steps of which are: the preparation of an aqueous dispersion based on BSA and SWCNT; preparation of substrates; deposition of BSA/SWCNT dispersion on substrates; application of water paste from SWCNT on substrates; irradiation of layers by lasers when they were in a liquid state; drying of samples; carrying out electrical and temperature measurements. Half of the layer was covered with a light-tight hollow box and the other half of the layer was laser irradiated. The laser irradiation of the layer was carried out for about 20 sec, at which time the layers completely became dry, while the other half of the layer remained in liquid. Conductivity was increased (70 ÷ 650) % by laser irradiation of the layers when they were in the liquid state. Maximum values of specific conductivity for BSA/SWCNT-1 S/m layers, and for layers SWCNT - 70 kS/m. The investigated electrically conductive layers of 99 wt.% BSA/0.3 wt.% SWCNT are promising for medical practice.

© Izdatel'stvo Meditsina. All rights reserved.  Introduction. Single-walled carbon nanotubes (SWCNTs) can create risks to human health when they enter the body by oral route when used in packaging materials, as promising agrochemicals and pesticides. The aim of the study. Evaluation of the subacute oral toxicity of SWCNT in rats. Material and methods. In the 92-days of the experiment, the SWCNTs were administered to rats along with drinking water at doses of 0 (control); 0.01; 0.1; 1.0 and 10 mg/kg body weight (BW) in the groups 1-5, respectively. Hematological indices of blood, apoptosis of hepatocytes, levels of pro- and anti-inflammatory cytokines in blood plasma and their production by cells of the spleen ex vivo, the content of the main and transient components of the intestinal microbiocenosis in the cecum were studied. There were determined hematological blood counts, hepatocyte apoptosis, levels of pro- and anti-inflammatory cytokines in blood plasma and their production by spleen cells ex vivo, content in the cecum of the main and transient components of the intestinal microbiocenosis. Results. At the SWCNT dose of 0.01 mg/kg BW there was a decrease in the number of neutrophils and basophils, an increase in the number of lymphocytes, and a decrease in the number and volume of platelets. At a dose of 0.1 mg/ kg bw there was noted a decrease in the number of cells in the early stage of apoptosis and the total number of cells in apoptosis, as well as a significant decrease in the levels of cytokines IL-10, IL-2, IL-4, IL-13, chemokine MIP-3a, TGF-β isoform 1; at a dose of 1.0 mg/kg IL-12p70, and TGF-β isoforms 1 and 3. TGF- β 2 level was significantly elevated in group 5. The suppressive effect was noted for SWCNTs on the mold flora in intestinal contents at all doses of nanomaterial used, whereas the number of yeasts increased at 1 mg/kg BW. The immunization of rats with ovalbumin had a clear modulating effect on the immunotropic effects of SWCNTs administered at a dose of 0.1 mg/kg BW in a 28-days experiment. Discussion. The mechanisms of the observed changes development are likely to be associated with both systemic anti-inflammatory effects and with a decrease in the effect of SWCNT on the permeability of the intestinal barrier to protein antigens and microbial toxins. Conclusion. SWCNTs exhibit a number of effects in relation to the studied indices that do not demonstrate a monotonic dependence on the dose of nanomaterial, which, apparently, is related to the processes of aggregation of the SWCNT.