UV-laser formation of 3D structures based on thermally stable heterochain polymers
|
15.07.2018 |
Dudova D.
Bardakova K.
Kholkhoev B.
Ochirov B.
Gorenskaia E.
Farion I.
Burdukovskii V.
Timashev P.
Minaev N.
Kupriyanova O.
|
Journal of Applied Polymer Science |
|
1 |
Ссылка
© 2018 Wiley Periodicals, Inc. A new approach to making a photopolymeric composition was first elaborated in this work based on the use of poly-N,N′-(m-phenylene)isophtalamide as the heterochain polymer matrix together with 4,4′-diphenyl oxide diacrylamide as the crosslinking agent. Reproducible three-dimensional (3D) objects have been formed using a laser stereolithograph completed with a laser with wavelength of 405 nm. According to the thermogravimetric analysis, the thermal stability of the formed objects could be changed through a control from 260 to 405 °C. Moreover, it was proven that the tensile strength of samples of the crosslinked films reached 90.1 ± 3.2 MPa at the elongation at break of 12.4 ± 2.3%, depending on the forming parameters of such samples. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018, 135, 46463.
Читать
тезис
|