Репозиторий Университета

© 2020 Elsevier Ltd The objective was to state zinc contribution in the effectiveness of novel zinc-doped dentin cements to achieve dentin remineralization, throughout a literature or narrative exploratory review. Literature search was conducted using electronic databases, such as PubMed, MEDLINE, DIMDI, Embase, Scopus and Web of Science. Both zinc-doping silicate and hydroxyapatite-based cements provoked an increase of both bioactivity and intrafibrillar mineralization of dentin. Zinc-doped hydroxyapatite-based cements (oxipatite) also induced an increase in values of dentin nano-hardness, Young's modulus and dentin resistance to deformation. From Raman analyses, it was stated higher intensity of phosphate peaks and crystallinity as markers of dentin calcification, in the presence of zinc. Zinc-based salt formations produced low microleakage and permeability values with hermetically sealed tubules at radicular dentin. Dentin treated with oxipatite attained preferred crystal grain orientation with polycrystalline lattices. Thereby, oxipatite mechanically reinforced dentin structure, by remineralization. Dentin treated with oxipatite produced immature crystallites formations, accounting for high hydroxyapatite solubility, instability and enhanced remineralizing activity.

© 2020 Elsevier Ltd The objective was to state zinc contribution in the effectiveness of novel zinc-doped dentin cements to achieve dentin remineralization, throughout a literature or narrative exploratory review. Literature search was conducted using electronic databases, such as PubMed, MEDLINE, DIMDI, Embase, Scopus and Web of Science. Both zinc-doping silicate and hydroxyapatite-based cements provoked an increase of both bioactivity and intrafibrillar mineralization of dentin. Zinc-doped hydroxyapatite-based cements (oxipatite) also induced an increase in values of dentin nano-hardness, Young's modulus and dentin resistance to deformation. From Raman analyses, it was stated higher intensity of phosphate peaks and crystallinity as markers of dentin calcification, in the presence of zinc. Zinc-based salt formations produced low microleakage and permeability values with hermetically sealed tubules at radicular dentin. Dentin treated with oxipatite attained preferred crystal grain orientation with polycrystalline lattices. Thereby, oxipatite mechanically reinforced dentin structure, by remineralization. Dentin treated with oxipatite produced immature crystallites formations, accounting for high hydroxyapatite solubility, instability and enhanced remineralizing activity.

© 2019 Elsevier B.V. This study aimed at evaluating the remineralization effect promoted by different bioactive fillers on simulated early caries lesions in enamel (ECLE). Forty sound bovine incisors were used to prepare buccal enamel specimens (6 × 6 × 2 mm). The specimens were divided into two areas (3 × 3 mm²): control (CTR) and experimental (EXP). All the enamel specimens were then submitted to a specific protocol for a period of 48 h to induce simulated caries lesions. Subsequently, the specimens were treated for 7 days (2 min, twice a day) with a slurry pastes containing different bioactive particles (P/L ratio: 1 g/mL). All the specimens were analyzed by laser speckle before and after treatments. The results showed after the first analysis that the ECLE had very low average intensity (back-scattered light). Conversely, after application of the bioactive pastes, higher average intensity was always detected; this was comparable to CTR sound specimens. In conclusion, innovative pastes/gels developed for enamel remineralization should contain bioactive particles that when applied daily on early caries lesions may “boost” the remineralization process to reestablish a sound enamel.

The purpose of the study was to assess the impact of toothpastes containing hydroxyapatite and fluoride on enamel caries resistance and remineralization rate. Study groups comprised 160 patients divided in 2 groups of 80 patients: 40 - at the age of 15-17 and 40 at the age of 18-25 who have been using toothpastes with hydroxyapatite and fluoride during 1 year. The plaque determination was carried out with the use of OHI-S and Turesky indexes. Litmus test pieces were used to determine oral fluid pH. The clinical determination of enamel remineralization rate, dynamics of acid resistance of enamel were carried out. Oral hygiene at baseline examination was poor in both groups. After oral hygiene training, there was a tendency towards indexes decrease more pronounced in the 18-25 age group regardless of the composition of the toothpastes used. Mean baseline oral fluid pH in the observation group was 6.5±0.4, in the comparison group - 6.8±0.4. By the end of the trial there was a tendency towards the increase of the oral fluid pH, which were 7.3±0.3 and 7.7±0.3, respectively. The enamel acid resistance of the patients of the observation group was significantly higher (p>0.05) compared with the group of patients using fluoride toothpaste, as well as the proportion of patients in whom the enamel recovery occurred within 24 hours (47.5% vs. 22.5%, respectively).

The purpose of our study was to assess the efficiency of toothpaste 'Intensive strengthening of supersensitive teeth with nano-GAP' INNOVA and the suspension 'Liquid Enamel' INNOVA on the sensitivity of teeth with gingival recession. We examined 40 people aged 20-25 years. Each group consisted of 20 people: 10 women, 10 men. The first group (observations) used the paste and the suspension for 14 days, and the second group (comparisons) cleaned teeth only with a brush without a paste. Schiff aerial test was performed to assess the rate of hypersensitivity. As a result of the study, it was found that the combination of paste and liquid suspension with nano-hydroxyapatite for 14 days effectively reduced the hypersensitivity of the teeth with gingival recession that was shown by a statistically significant decrease in the Schiff index in the observation group. Thus, this combination is the method of choice in the treatment of hyperesthesia and can be used as an alternative substitute therapy.